| in doubled hexagonal-design with threaded inserts out of steel(9 S 20 K zinc coated) |
| |
|
|
| The offered standoff insulators are manufactured by a glas-fibre
reinforced unsalturated polyester resin. The special characteristic
is a doubled-hexagonal-design. Soyou find a hexagonal
area at the top as well as at the bottom of the insulator. Both hexagonal
areas are displaced against each other. The design enable a quick
and easy installationwithout problem. This keeps installation costs
down to a minimum. |
| |
|
|
 |
|
  |
| |
|
Testing procedure for breaking strength |
| |
|
|
| Part-No. |
dimensions mm |
PS
kV |
BWS
kV |
F
kN |
Z
kN |
weight
kg / % Stck. |
| D |
H |
G |
SW |
T |
H1 |
| 03068
S |
30 |
30 |
M 6 |
24 |
8 |
9,5 |
5 |
0,75 |
3 |
6 |
5,70 |
| 03069
S |
|
|
M 8 |
|
|
|
|
|
|
|
5,40 |
| 03070
S |
30 |
40 |
M 6 |
|
10 |
10 |
5 |
1,00 |
4 |
8 |
7,30 |
| 03071
S |
35 |
30 |
M 6 |
30 |
8 |
10 |
5 |
0,75 |
4 |
7 |
6,50 |
| 03072
S |
|
|
M 8 |
|
|
|
|
|
5 |
8 |
6,10 |
| 03073
S |
40 |
40 |
M 8 |
32 |
12 |
10,5 |
5 |
1,00 |
6 |
11 |
13,00 |
| 03074
S |
|
|
M 10 |
|
11 |
|
|
|
|
|
12,10 |
| 03075
S |
M 12 |
10 |
11,20 |
| 03080
S |
40 |
50 |
M 8 |
32 |
12 |
10,5 |
10 |
1,50 |
5 |
11 |
16,50 |
| 13080
S |
|
|
M 10 |
|
15 |
|
|
|
|
|
16,50 |
| 03081
S |
M 12 |
|
13 |
|
7 |
|
13,80 |
| 13081
S |
40 |
60 |
M 8 |
32 |
12 |
11 |
10 |
1,5 |
4 |
11 |
16,90 |
| 13082
S |
|
|
M 10 |
|
15 |
|
|
|
|
|
17,60 |
| 03078
S |
50 |
40 |
M 10 |
41 |
11 |
13 |
5 |
1,00 |
8 |
13 |
16,50 |
| 03079
S |
|
|
M 12 |
|
10 |
|
|
|
10 |
|
16,50 |
| 13083
S |
50 |
50 |
M 12 |
41 |
13 |
13,5 |
10 |
1,50 |
8 |
13 |
20,00 |
| 03084
S |
50 |
60 |
M 10 |
|
15 |
|
|
|
6 |
|
24,10 |
| 03085
S |
|
|
M 12 |
18 |
7 |
24,70 |
| 13084
S |
60 |
60 |
M 12 |
50 |
18 |
18,5 |
10 |
1,50 |
9 |
15 |
32,30 |
| 13085
S |
|
|
M 16 |
|
17 |
|
|
|
12 |
17 |
32,80 |
| F = Force limitation rating at ins. top edge |
|
| Z = Tensile force |
|
| PS = Testing voltage |
|
| BWS = max. AC operating voltage |
|
| Technical datas of the material |
|
| spec. weight |
DIN 53479 |
1,75 g/cm³ |
| flexural strength |
DIN 53452/ISO R 178 |
120 N/mm² |
| impact strength |
|
| notched impact
strength |
DIN 53453/ISO R 179 |
45 kJ/m² |
| max permissable operation temp. |
VDE 0304 Teil 21 |
+ 130° C |
| resistance to heat |
DIN 53459-A/ISO R 181 |
Step 2a |
| flammability |
UL 94 |
Klasse V-O |
| surface resistivity |
DIN 53482 |
1013 Ohm |
| specific volume resistivity |
DIN 53482 |
1014 Ohm x cm |
| dielectric dissipationfactor |
DIN 53483 |
< 0,02 tan /50 Hz |
| tracking resistance |
DIN IEC 112
VDE 0303 Teil 1 |
CTJ 600 |
| water absorption |
DIN 53495 |
< 50 mg/1 d |
| colour |
- |
brown RAL 8016 |
| The values in the table have been
determined with our own standards based on DIN 53451 and combined with the standards for the respective materials for test purposes. |
|
| |
|
|
|
| |
|
|